Qingdao Crown Chemica_insoluble sulfur_petroleum resin_ functional resin-

Phenolic Resin

DETAILED DESCRIPTION

		composition	Appearance	Soft Point ℃	Gel time Min	Free Phenol %	Acid value mgKOH/g	Ash %	Volatile % @105℃, 2h	Application
Tackifying Resin	1100 Series	P- Tert-Octyl Phenol-Formaldehyde	White to light yellow pieces/particles	85~135	-	≤4.0	30~54	@600℃ <0.5	-	The alkyl of the p-teroctyl phenol formaldehyde viscosifying resin is in the counterpoint of the phenolic hydroxyl group, and no chemical reaction at the curing temperature, with non-thermal reactivity.
	7001 Super	Alkylphenol Acetylene	Brown grannular/particles	135~150	-	-	-	@750℃ <1.0	-	This product is called super tackifying resin. It can make all kinds of rubber with excellent properties such as long-term viscosifying, high temperature and humidity resistance, low dynamic compression heat generation and so on.
	1560 Super	Para-Tert-Butyl Phenol-Formaldehyde	White to light yellow pieces/particles	126~140	-	<3.0	25~60	@600℃ <0.5	≤0.5	Used as synthetic rubber and natural rubber adhesion promoter, especially for butyl benzene, nitrile, neoprene, suitable for high viscosity requirements of tire and rubber products, and easy to dissolve, no dust.
Reinforcing Resin	2101	Tall oil modified Phenol- Formaldehyde	Brown pieces/particles	92~103	@130℃，10%HEXA 5.5~7.5	≤2.5		@800℃ ≤0.5		Used together with methylene donor, such as HMT or HMMM, the hot curing reaction can improve the hardness, tear strength, wear resistance, strength and elongation of the adhesive.
Reinforcing Resin	2201	Cashew nut shell oil modified Phenol- Formaldehyde	Bronzing pieces/particles	90-102	@130℃，10%HEXA 4.0~7.0	≤2.0		@800℃ ≤0.5		Reduce viscosity during rubber compound processing and is conducive to the dispersion of fillers, and prolong the role of coke burning time, mainly applied in the bead.
Bonding Resin	3100 Series	Resorcinol- Formaldehyde	Bronzing granule/ particles	98~110	@120℃，10%HEXA 2.0~3.5	1.5~4.0			≤0.5	Resorcinol -formaldehyde and methylene vulcanize rapidly under vulcanizing temperature. Stress at definite elongation of vulcanized rubber decrease. Tensile and adhesive strength increase. Good bonding performance makes the adhesive strength between the material and fiber or wire much higher. Thus it can improve durability of the tire.
Curing Resin	4000 Series	Alkylphenol formaldehyde resin with methylol group	Yellowish block(flake)	100~125						The main component is to the tert-butyl phenolic thermal reaction resin, is an adhesive,. mainly used for neoprene adhesive, suitable for contact adhesive formnula system, with highviscosity, high temperature stability, low elongation and other excellent performnance.